Description
Specifications
High UV and weather resistance
Very easy to work with, high final hardness, lasting gloss
Chromate-free and lead-free
Benefits
Long service life
Efficient working
Low environmental impact
Application
Surface treatment for use in the industrial sector, for tractors, agricultural machines and civil engineering machinery
For iron and steel
Resistant to benzine and diesel oil for short-term contact
Properties
Bonding agent base: modified alkyd resins
Dry solids: 52-58%
Basic viscosity (DIN 53 211): thixotropic
Specific weight (DIN 51 757): 0.97–1.18 kg/l
Gloss level (DIN 67 530) >80%/60° (high gloss)
Temperature resistance: continuous load 130°C, short-term load 150°C
Application conditions: from +10°C and up to 80% relative humidity
Set to touch after 6–8 hours (at 20°C)
Hardened after 24 hours (at 20°C)
Final hardness after 3–4 days (at 20°C)
Base coat: Kramp primer (coat thickness: 50–60 µm)
Top coat: Kramp synthetic resin varnish (coat thickness: 50–60 µm)
Theoretical coverage per litre: 7,5–8,0 m²/kg (with a coat thickness of 50 µm)
Technical information
Surface preparation: The object to be treated must be thoroughly cleaned, degreased and sanded as necessary
Some types available in semi-gloss finish and matt
Complies with Austrian Solvents Ordinance (dated 1/1/96)
Drying times can be shortened by using Kramp quick-drying thinners instead of Kramp synthetic resin thinners
Lower temperatures result in longer drying times
Base colour
White
Base
Synthetic resin
Brand colour
n/a
Designed for material
Metal
Content
1 l
RAL colour code
9010
Dust dry time
30-60 min
Packing type
Can