Description
Specifications
Can also be applied as a thick layer
Quick drying
Active corrosion protection (zinc phosphate)
Benefits
High coverage
Saves time
Ensures a long service life
Application
Suitable for iron and steel
Properties
Can be coated with 1K and 2K varnishes
Base coat: Kramp primer (coat thickness: 50–60 µm)
Can be stored outside for up to 5 days without a final coating layer
High filling capability
For electrostatic processing
Temperature resistance: continuous load 120°C, transient load 150°C
Dry matter content: 65–70%
Basic viscosity (DIN 53 211): thixotropic
Specific weight (DIN 51 757): 1.4–1.5 kg/l
Gloss (DIN 67 530): 10–20%/60° (matt)
Chromate-free and lead-free
Adhesion (DIN 53 151): iron, steel: class 0 (very good)
Technical information
Processing conditions: from +10°C and up to 80% relative humidity
Surface preparation: The object to be treated must be thoroughly cleaned, degreased and sanded as necessary
Dust-dry after 15–20 minutes (at 20°C)
Set to touch after 45–60 minutes (at 20°C)
Set to touch after 4–5 hours (at 20°C)
Final hardness after 3–4 days (at 20°C)
Using Kramp rapid drying hardener can reduce drying times
Lower temperatures result in longer drying times
Base colour
Red
Brown
Base
Synthetic resin
Brand colour
n/a
Designed for material
Metal
Content
1 l